Polyurethane Materialius Relatio | |
Prepolymer Caracteristicae | |
%NCO |
5.0±0.2 |
Apparitio @20℃ |
Solidum Album |
Viscositas @80℃/mPa·s |
1200 |
Conditiones fundendi, h/℃, 20L |
12/80 |
Technologia processus | |
Agentia solidificans |
MOCA |
Coeficientis extensionis catenae (NH,/NCO) |
0.9 |
Dosage agentiae solidificantis (per 100 partes praepolymereum) |
14.3 |
Temperatura praepolymери/℃ |
80 |
Temperatura agentis solidificantis/℃ |
110 |
Temperatura formae recommendata/℃ |
100 |
Tempus gelationis/min (400g mixturae) |
4-6 |
Tempus exformandi/min (400g mixturae) |
20-30 |
Solidificatio postea, h@℃ |
16/100 |
Proprietates physicae elastomerorum | |
Fortitudo @ 20℃, Shore A |
95±2 |
Vis Extensio\/MPa |
58.6 |
modulus ad 100%/MPa |
10.8 |
300% modulus/MPa |
25.6 |
Elongatio ad rupturam / % |
560 |
Robur lacerationis/(angulus rectus, KN/M) |
118 |
Rebound/% |
34 |
DIN volutus usus/mm³ |
45 |
Non. |
Typus |
H |
Pix |
L*W*H |
Bolt |
D*d |
1 |
230BB |
16 |
101 |
230*70*37 |
M12*25 |
170*0 |
2 |
250BA |
16 |
101 |
250*70*37 |
M12*25 |
200*0 |
3 |
300BA |
101 |
16 |
300*70*37 |
M12*25 |
200*0 |
4 |
300BB |
101 |
16 |
300*70*37 |
M12*25 |
200*0 |
5 |
450BA |
135 |
14 |
450*106*37 |
M12*25 |
350*46 |
6 |
400BA |
135 |
14 |
400*106*37 |
M12*25 |
300*46 |
7 |
500BA |
171 |
20 |
500*136*54 |
M16*30 |
400*60 |
8 |
600BA |
190 |
26 |
600*140*67 |
M20*35 |
400*69 |
EN